ESAB offers a complete line of welding and cutting products and solutions. Explore our equipment offering with ease based on product line and industry.
ESAB is a world leader in welding and cutting equipment and consumables. Explore our complete line of welding & cutting products for virtually every application.
ESAB University is your online learning destination for welding and fabrication technology. Make personalized playlists of your favorite resources including videos, blogs, articles, webinars and more.
ESAB Courses are structured learning paths designed to take your welding knowledge and skills to the next level.
Articles cover industry topics more in-depth and are created in partnership with ESAB engineers and master welders. Click the links to see the latest.
ESAB blogs include information and tips from ESAB Experts to improve your welding and fabrication knowledge.
ESAB University videos are curated with tips and best practices from top fabricators around the world. Learn new techniques or improve your current skills with ESAB University videos.
Enhance your knowledge of welding, cutting, and fabrication with free and accessible webinars on a variety of topics, including welding best practices, tips for using ESAB products, new product launches, and more, presented by trusted ESAB experts.
ESAB's Future for Fabricators platform is committed to highlighting those who lead education for aspiring future fabricators. We aim to share inspirational stories, facilitate initiatives to bring tools and expertise to communities and make our equipment accessible to ensure future fabricators are set up for success - right from the start.
ESAB is a world leader in welding and cutting equipment and consumables. We offer a complete line of fabrication solutions for virtually every application.
ESAB Newsroom - Stay up to date with the latest news from ESAB. View press releases, product announcements, corporate news, and more here.
ESAB EHS (Environment, Health & Safety) initiatives are monitored with the highest degree of importance and commitment to safety is ingrained in our culture.
The history of ESAB is the History of Welding. Go here to view an interactive look at ESAB's history in shaping the future of innovation in welding, cutting, and fabrication.
View available job openings and more on the ESAB Careers page.
ESAB offers a wealth of product support resources, including a range of technical and service publications, from Safety Data Sheets and downloadable product manuals to product certifications.
Visit ESAB's global manual search engine to access the items below and more.
Global User Manuals
Instruction Manuals
Spare Parts List
Product Storage Instructions
View Main Contact Page
View ESAB Location Information
No playlist found! Your playlist can be created here.
Many fabricators experience welding problems at different times of the year. Moisture (H20) is a prime source of hydrogen. At arc temperatures, water breaks down releasing hydrogen atoms that cause porosity in weldments. Shielding gas supplies are controlled to very low moisture content (-70°F dewpoint or lower). Likewise, the atmospheric conditions in a fabricating facility need to be controlled to prevent moisture condensation from forming on the electrode or base metal.
Aluminum, that is allowed to repeatedly come into contact with water, will eventually form a hydrated oxide (AIOH) coating. Moisture from condensation present on either the electrode or the base metal can cause two problems during welding:
Porosity is caused by hydrogen generated from the breakdown of water or the breakdown of hydrated oxide (AIOH) present on metal surfaces.Entrapment of the actual oxide (AIOH), present on the metal surfaces, in the weldment.
Relative Humidity - The ratio of the quantity of water vapor present in the atmosphere to the quantity that would saturate the air at the existing temperature. Relative humidity is expressed as a percentage number and needs to be monitored in the welding area. Dip tanks, cleaning stations, etc., affect relative humidity.
Dew Point - The temperature at which water vapor condensation in the air occurs. Moisture will condense on metal surfaces when their temperature equals or below the dew point. For each relative humidity percentage, there is a corresponding dew point.
Air Temperature - The temperature of the air in the welding area at any given time.
Metal or Electrode Temperature - The electrode or base metal temperature at any given time.
DEW POINT CONDITIONS VERSUS RELATIVE HUMIDITY:
Relative Relative(Tair-Tmetal)º Humidity (Tair - Tmetal)º Humidity ºC (ºF) % ºC (ºF) %___________________________________________________ 0 (0 ) 100 12 (21.6) 44 1 (1.8) 93 13 (23.4) 41 2 (3.6) 87 14 (25.2) 38 3 (5.4) 81 15 (27.0) 36 4 (7.2) 75 16 (28.8) 34 5* (9.0*) 70* 18 (32.4) 30 6 (10.8) 66 20 (36.0) 26 7 (12.6) 61 22 (39.6) 23 8 (14.4) 57 24 (43.2) 21 9 (16.2) 53 26 (46.8) 18 10 (18.0) 50 28 (50.4) 16 11 (19.8) 48 30 (54.0) 14___________________________________________________
(Tair - Tmetal)º- Temperature of the air minus the temperature of the metal shown in ºC and ºF.
The above chart shows the relative humidity at which detrimental water condensate will form for several given differential temperatures.
* Example - If the relative humidity in the weld area is 70%, the base metal and electrode must be no colder than 9ºF below the air temperature to prevent moisture condensation.
In an aluminum welding shop, the uniformity of air and metal temperatures is important especially when the relative humidity is high. The welding electrode and base metal should be allowed to stabilize to the weld area temperature. The electrode should not be opened in the weld area for 24 hours after entry from a cooler storage area. The base metal should be cleaned and brushed with a clean stainless steel brush before welding. AlcoTec recommends mild alkaline solutions and commercial degreasers that do not evolve toxic fumes during welding. Welders should wipe joint edges with a clean cloth dipped in a volatile petroleum-based solvent. All surfaces must be thoroughly dried after cleaning.